BEAMIT | Hastelloy X | An exceptional combination of oxidation resistance, ease of fabrication and high temperature strength

Hastelloy X

 

Hastelloy X 

DMLS - Hastelloy X by BEAMIT

Hastelloy X

Hastelloy X is a Nickel-Chromium-Iron-Molybdenum alloy with an exceptional combination of oxidation resistance, ease of fabrication and high temperature strength.
It has also been found to be exceptionally resistant to stress corrosion cracking in petrochemical applications.

> 99,9%
Density

Chemical Composition

  • Ni balance
  • Cr 20,500 / 23,000
  • Fe 17,000 / 20,000
  • Mo 8,000 / 10,000
  • Co 0,500 / 2,500
  • W 0,500 / 0,900
  • Ti - / 0,150
  • Al - / 0,200
  • Mn - / 0,200
  • Si - / 1,000
  • C - / 0,100
  • B - / 0,010
  • P - / 0,040
  • S - / 0,015
  • Cu - / 0,500
  • Se - / 0,005
  • O - / 0,030
  • N - / 0,015
  • Mechanical Proprieties

    Tensile
    properties
    at
    room temperature
     
    As Built Annealing (Pre-HIP) Annealed (Pre-HIP) + HIP + Annealed (Post-HIP)
    Z XY Z XY Z XY
    Mean ± std. Dev. Mean ± std. Dev. Mean ± std. Dev. Mean ± std. Dev. Mean ± std. Dev. Mean ± std. Dev.
    UTS [MPa] 719 ± 35 811 ± 40 672 ± 20 726 ± 35 667 ± 25 708 ± 35
    Yield Strenght [MPa] 528 ± 30 613 ± 40 384 ± 25 391 ± 25 364 ± 20 358 ± 30
    Elongation at break [%] 37 ± 9 35 ± 4 52 ± 4 45 ± 3 57 ± 4 47 ± 4
    Young's Modulus [GPa] 167 ± 30 188 ± 30 190 ± 45 190 ± 25 204 ± 25 210 ± 30
    Tensile properties at +820°C ± 10°C
     
     
    Annealed (Pre-HIP)
    Z
    Mean ± std. Dev.
    UTS [MPa] 355 ± 5
    Yield Strenght [MPa] 282 ± 5
    Elongation at break [%] 58 ± 5
    Hardness
     
     
    As Built Annealed (Pre-HIP) Annealed (Pre-HIP) + HIP + Annealed (Post-HIP
    HV HV HV
    HV/HRC min 220 199 220

    This site uses its own and third-party technical cookies, for analytical and statistical purposes. By clicking on , Accept, closing this banner, continuing to browse or making another positive action on this web page, the visitor consents to the use of cookies. For more information or to refuse consent to the use of certain cookies, see the privacy policy: Read more