BEAMIT | Stainless Steel - 15-5 PH | Perfect for the creation of functional metal prototypes

15-5 PH

Stainless Steel

15-5 PH - Stainless Steel

DMLS - Stainless Steel 15-5 PH by BEAMIT

Stainless Steel 15-5 PH

Stainless Steel 15-5 PH is a martensitic precipitation-hardening stainless steel that provides high strength, good corrosion resistance, good mechanical properties at temperatures up to 600°F (316°C) and good toughness in both the longitudinal and transverse directions in both base metal and welds.

> 99,6%
Density

Chemical Composition (%wt)

  • Fe balance
  • Cr 14,500 / 15,500
  • Ni 3,500 / 5,500
  • Cu 2,500 / 4,500
  • Nb + Ta 0,150 / 0,450
  • Mn - / 1,000
  • Si - / 1,000
  • P - / 0,040
  • S - / 0,030
  • O - / 0,100
  • C - / 0,070
  • N - / 0,100
  • Mechanical Proprieties

    Tensile
    properties
    at
    room temperature
     
    As Built
    Z XY
    Mean ± std. Dev. Mean ± std. Dev.
    UTS [MPa] 1037 ± 30 994 ± 25
    Yield Strenght [MPa] 937 ± 25 965 ± 25
    Elongation at break [%] 14 ± 3 15 ± 3
    Young's Modulus [GPa] 192 ± 15 199 ± 20
    Hardness
     
     
    As Built H900 BEAMIT
    HV HRC HV HRC
    HV/HRC min 280 27 389 39

    This site uses its own and third-party technical cookies, for analytical and statistical purposes. By clicking on , Accept, closing this banner, continuing to browse or making another positive action on this web page, the visitor consents to the use of cookies. For more information or to refuse consent to the use of certain cookies, see the privacy policy: Read more