AISI 316 L - Stainless Steel

AISI 316L Stainless Steel
AISI 316L Stainless Steel: this steel is renowned for its high mechanical properties and its first-class corrosion resistance.
It is ideal for the construction of medical instruments, automotive and industrial spare parts.
> 99,9%
Density
Chemical Composition
- Fe balance
- Cr 16,000 / 18,000
- Ni 10,000 / 14,000
- Mo 2,000 / 3,000
- Mn - / 2,000
- Si - / 1,000
- P - / 0,015
- S - / 0,015
- O - / 0,040
- C - / 0,030
Mechanical Proprieties
Tensile properties at room temperature |
As Built | Annealed | ||
---|---|---|---|---|
Z | XY | Z | XY | |
Mean ± std. Dev. | Mean ± std. Dev. | Mean ± std. Dev. | Mean ± std. Dev. | |
UTS [MPa] | 481 ± 25 | 591 ± 20 | 492 ± 25 | 576 ± 20 |
Yield Strenght [MPa] | 379 ± 20 | 482 ± 20 | 310 ± 15 | 357 ± 20 |
Elongation at break [%] | 15 ± 4 | 35 ± 10 | 21 ± 3 | 34 ± 3 |
Young's Modulus [GPa] | 159 ± 15 | 151 ± 15 | 173 ± 20 | 167 ± 10 |
Hardness |
As Built | Annealed | ||
---|---|---|---|---|
HV | HRC | HV | HRC | |
HV/HRC min | 280 | 27 | 160 | - |